34CrNiMo6 Alloy Steel Round Bar Diameter 10 - 350mm in 6m Length EN
DIN GB ASTM Standard
Products Specification
| Products Name | Alloy 34CrNiMo6 Steel Round Bar |
| Diameter | 10 - 300mm |
| Length | 6m or custom cutting any length as request |
| Type | Hot Rolled |
| Brand | BAOSTEEL DELTA DONGBEI HUAXI SHAGANG.etc |
| MOQ | 1 Ton |
| Loading Port | Shanghai Port |
| Packing | packing by steel wire rope |
| Deliver time | 5 - 7 days for stock materials |
| Other Grade | Q195,Q235,10#,20#,35#,45#,Q215,Q345,12Cr1Mov, 15CrMo,304,316,20Cr,40Cr,20CrMo,35CrMo,42CrMo, 40CrNiMo,GCr15,65Mn,50Mn,50Cr,3Cr2W8V,20CrMnTi,5CrMnMo
,30CrNiMo8,34CrNiMo6 |
| Standard | ASTM GB EN DIN |
| Application | Structure and Industrial |
Regular Standard Size of our 30CrNiMo8 Round Bar in Stock
| Standard Diameter | 10 12 15 18 20 25 30 35 40 45 50 55 60 65 70 75 80 85 90 95 100 105
110 120 130 140 150 160 180 200 210 220 230 250 270 300 320 330
350mm |
1.EN Steel 34CrNiMo6 Supply Range
Round Steel Bar Sizes: diameter 10mm – 2000mm
Steel Flat and Plate: 10mm-1500mm thickness x 200-3000mm width
Other steel shape and sizes available according to your
requirements.
Surface finish: Black, machined, peeled, turned or according to
other customers’ pecial requirements.
2.EN 34CrNiMo6 Steel Standards And Equivalents
| BS EN 10083 -3: 2006 | 34CrNiMo6 / 1.6582 | ASTM A29: 2004 | 4337 |
| BS EN 10250 – 3: 2000 |
3. EN/DIN 34CrNiMo6 Steel Chemical Composition Properties
| BS EN 10083 – 3:2006 | 34CrNiMo6
/1.6582 | C | Mn | Si | P | S | Cr | Mo | Ni |
| 0.30-0.38 | 0.5-0.8 | 0.40 max | 0.025 max | 0.035 max | 1.3-1.7 | 0.15-0.30 | 1.3-1.7 |
| BS EN 10250-3:2000 | C | Mn | Si | P | S | Cr | Mo | Ni |
| 0.30-0.38 | 0.5-0.8 | 0.40 max | 0.035 max | 0.035 max | 1.3-1.7 | 0.15-0.30 | 1.3-1.7 |
| ASTM A29: 2004 | 4337 | C | Mn | Si | P | S | Cr | Mo | Ni |
| 0.30-0.40 | 0.6-0.8 | 0.20-0.35 | 0.035 max | 0.040 max | 0.70-0.90 | 0.20-0.30 | 1.65-2.00 |
4.Mechanical Properties of EN/DIN 34CrNiM06 / 1.6582 Alloy Steel
| Properties | < 16 | >16 – 40 | >40 – 100 | >100 – 160 | >160 – 250 |
| Thickness t [mm] | < 8 | 8<t<20 | 20<t<60 | 60<t<100 | 100<t<160 |
| Yield strength Re [N/mm²] | min. 1000 | min. 900 | min. 800 | min. 700 | min. 600 |
| Tensile strength Rm [N/mm2] | 1200 – 1400 | 1100 – 1300 | 1000 – 1200 | 900 – 1100 | 800 – 950 |
| Elongation A [%] | min. 9 | min. 10 | min. 11 | min. 12 | min. 13 |
| Reduction of area Z [%] | min. 40 | min. 45 | min. 50 | min. 55 | min. 55 |
| Toughness CVN [J] | min. 35 | min. 45 | min. 45 | min. 45 | min. 45 |
5.Heat Treatment of 34CrNiMo6 Engineering Steel
Quenched and Tempered (Q+T) of 34CrNiMo6 Steel
- Heat 34CrNiMo6 round steel slowly to the temperature of 850°C;
- Soak at this hardening temperature quench in oil;
- Temper as soon as 34CrNiMo6 steels reach room temperature.
- Heat uniformly to the suitable temperature;
- Withdraw from the furnace and cool in the air.
- The usual tempering temperature is 600°C which depending on the
actual requirements.
6.Forging of DIN 34CrNiMo6 / 1.6582 Steel
Hot forming temperature: 1100-900oC.
7.Machinability of Steel 34CrNiMo6
Machining is best done with this 1.6582 alloy steel in the annealed
or normalized and tempered condition. It can be machined by all
conventional methods.
8.Welding
The alloy materials can be fusion or resistance welded. Preheat and
post heat weld procedures should be followed when welding this
alloy by established methods.
9.Application
EN DIN 34CrNiMo6 steel is used to make tools which demands good
plasticity and high strength. It is usually selected to make the
big size and important parts, such as heavy machinery axle,turbine
shaft blade, high load of transmission parts, fasteners, crank
shafts, gears, as well as heavily loaded parts for motor
construction etc.